Resins for Shoes

PU resin for shoe soles

Huada Chem Group, as an early enterprise in the production of polyurethane resins for footwear, has always adhered to provide customers with stable and high quality products and constantly enriched their product lines. Customized development services can be provided according to the personalized needs of customers.

HuaDa chem group
Jiangsu Huada
1
High Hardness Polyester High hardness polyester
HT-5890T/F-2280
1. Characteristic：High hardness with medium-low density
2. Application: High-heel soles and platform soles
3. Typical characteristics of PU matrix
Product name Appearance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-5890T liquid or waxy solid 600~1000 1.160~1.180 18
F-2280 liquid or waxy solid 300~700 1.180~1.200 20
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-5890T 60-70℃ preheating for 6~8h
F-2280 60-70℃ preheating for 8~12h
5. Processing & Reaction Parameters
Item Material temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Foam density (g/cm3) Mold temperature(℃) Demolding time(min)
Technical parameters 40~45/40~45 100/116~118 7~10 40~60 0.24~0.27 45~55 3~5
◎The addition amount of Catalyst SM-2 is 250±5g/18kg
◎Water and hardener added as required
6. Product properties
Item Molding density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing resistance test at 23℃
Physical property value 0.50~0.65 80~90 50~58 320~400 32~37 300,000 cycles without cracks
◎Tested on 6mm-thick samples.
◎Free foam density may vary with temperature & humidity.
◎ Demolding time increases with product thickness. 
◎Data provided are for reference only. Detailed specifications are subject to actual operating conditions. For additional physical property requirements, please contact us.
HT-5885B/F-2260
1. Characteristics: High hardness, medium-low density
2. Application: Standing heel sole, high wedge heel
3. Typical characteristics of PU matrix
Product name Appearance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package (kg)
HT-5885B Liquid or wax-like 600~1000 1.160~1.180 18
F-2260 Liquid or wax-like 300~700 1.180~1.200 20
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-5885B 60-70℃ preheating for 6~8h
F-2260 60-70℃ preheating for 8~12h
5. Molding conditions and reaction parameters
Item Material temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time (s) Rise time (s) Foam density (g/cm3) Mold temperature(℃) Demolding time (min)
Technical parameters 40~45/40~45 100/135~137 6~9 30~38 0.20~0.23 45~55 3~5
◎The addition amount of Catalyst SM-2 is 250±5g/18kg
◎Water and hardener are added according to actual needs 
6. Product properties
Item Molding density(g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation (%)  Tear strength (kg/cm) Flexing resistance test at 23℃
Physical property value 0.40~0.45 85~92 50~63 320~400 30~35 300,000 cycles without cracks
◎This physical property data was obtained from testing a 6mm thick test piece.
◎Free foam density will vary according to the season (temperature, humidity).
◎Demolding time will be prolonged as the thickness of the finished product increases.
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
2
Medium Hardness Polyester Medium hardness polyester
HT-5606/F-2180
1. Characteristics: bright surface, soft hand feeling
2. Application: Leather shoes, sandals
3. Typical characteristics of PU matrix
Product name Appearance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package (kg)
HT-5606 Liquid or wax-like 800~1200 1.120~1.200 18
F-2180 Liquid or wax-like 200~600 1.190~1.210 20
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-5606 60-70℃ preheating for 6~8h
F-2180 60-70℃ preheating for 8~12h
5. Molding conditions and reaction parameters
Item Material temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time (s) Rise time (s) Foam density (g/cm3) Mold temperature(℃) Demolding time(min)
Technical parameters 40~45/40~45 100/99~101 7~10 50~60 0.23~0.30 45~55 3~5
◎The addition amount of Catalyst SM-2 is 240±5g/18kg
◎Water and hardener are added according to actual needs 
6. Product properties
Item Molding density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation (%) Tear strength (kg/cm) Flexing resistance test at 23℃
Physical property value 0.55~0.65 58~65 50~57 370~450 33~40 300,000 cycles without cracks
◎This physical property data was obtained from testing a 6mm thick test piece.
◎Free foam density will vary according to the season (temperature, humidity).
◎Demolding time will be prolonged as the thickness of the finished product increases.
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
HT-5608B/F-2180
1. Characteristics: medium density, good moldability
2. Application: Casual shoes, sandals
3. Typical characteristics of PU matrix
Product name Appearance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package (kg)
HT-5608B Liquid or wax-like 500~900 1.160~1.180 18
F-2180 Liquid or wax-like 200~600 1.190~1.210 20
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-5608B 60-70℃ preheating for 6~8h
F-2180 60-70℃ preheating for 8~12h
5. Molding conditions and reaction parameters
Item Material temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time (s) Rise time (s) Foam density (g/cm3) Mold temperature(℃) Demolding time (min)
Technical parameters 40~45/40~45 100/116~118 9~11 40~60 0.22~0.25 45~55 3~5
◎The addition amount of Catalyst SM-2 is 270±5g/18kg
◎Water and hardener are added according to actual needs 
6. Product properties
Item Molding density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation (%)  Tear strength  (kg/cm) Flexing resistance test at 23℃
Physical property value 0.46~0.55 60~65 48~55 350~450 32~37 300,000 cycles without cracks
◎This physical property data was obtained from testing a 6mm thick test piece.
◎Free foam density will vary according to the season (temperature, humidity).
◎Demolding time will be prolonged as the thickness of the finished product increases.
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
HT-5650/F-2280
1. Characteristics: Good moldability, lightweight
2. Application: Women's shoes, casual shoes
3. Typical characteristics of PU matrix
Product name Appearance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Packaging (kg)
HT-5650 Liquid or wax-like 800~1200 1.160~1.180 18
F-2280 Liquid or wax-like 200~600 1.180~1.200 20
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-5650 60-70℃ preheating for 6~8h
F-2280 60-70℃ preheating for 8~12h
5. Molding conditions and reaction parameters
Item HT/F Material temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time (s) Rise time (s) Foam density (g/cm3) Mold temperature(℃) Demolding time(min)
Technical parameters 40~45/40~45 100/84.5~86.5 7~10 30~40 0.22~0.26 45~55 3~5
◎The addition amount of Catalyst SM-2 is 300±5g/18kg 
◎Water and hardener are added according to actual needs 
Water H2O 35±5g/18kg
6. Product properties
Item Molding density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation (%) Tear strength (kg/cm) Flexing resistance test at 23℃
Physical property value 0.45~0.55 58~65 45~60 370~470 30~35 300000 times without cracks
◎This physical property data was obtained from testing a 6mm thick test piece.
◎Free foam density will vary according to the season (temperature, humidity).
◎Demolding time will be prolonged as the thickness of the finished product increases.
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.

3
Soft Polyester Soft polyester
HT-5830L/F-2580L
1. Characteristics: low hardness, good hand feeling, cold resistance
2. Application: Cemented shoes and casual shoe soles
3. Typical characteristics of PU matrix
Product name Appearance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package (kg)
HT-5830L Liquid or wax-like 800~1200 1.170~1.190 18
F-2580L Liquid or wax-like 300~700 1.180~1.200 20
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-5830L 60-70℃ preheating for 6~8h
F-2580L 60-70℃ preheating for 8~12h
5. Molding conditions and reaction parameters
Item HT/F Material temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time (s) Rise time (s) Foam density (g/cm3) Mold temperature(℃) Demolding time (min)
Technical parameters 40~45/40~45 100/54.5~56.5 7~10 40~60 0.21~0.25 45~55 3~5
◎The addition amount of Catalyst SM-2 is 300±5g/18kg
◎Water and hardener are added according to actual needs
6. Product properties
Item Molding density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation (%) Tear strength (kg/cm) Flexing resistance test at -20℃
Physical property value 0.42~0.50 30~40 30~50 500~700 15~25 40000 cycles without cracks
◎This physical property data was obtained from testing a 6mm thick test piece.
◎Free foam density will vary according to the season (temperature, humidity).
◎Demolding time will be prolonged as the thickness of the finished product increases.
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
HT-5835/F-2280
1. Characteristics: low hardness, good hand feeling, hydrolysis resistance
2. Application: Cemented shoes and casual shoes
3. Typical characteristis of PU matrix
Product name Appearance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Packaging (kg)
HT-5835 Liquid or wax-like 1000~1800 1.110~1.130 18
F-2280 Liquid or wax-like 200~600 1.180~1.200 20
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-5835 60-70℃ preheating for 6-8h
F-2280 60-70℃ preheating for 8~12h
5. Molding conditions and reaction parameters
Item
HT/F Material temperature (℃)		 Mixing ratio (HT+SM)/F(By weight) Cream time (s) Rise time (s) Foam density (g/cm3) Mold temperature(℃) Demolding time (min)
Technical parameters/td> 40~45/40~45 100/62~64 7~10 40~60 0.21~0.25 45~55 3~5
◎The addition amount of Catalyst SM-2 is 350
◎Water and hardener are added according to actual needs
6. Product properties
Item Molding density Hardness Tensile strength Elongation Tear strength Flexing endurance test
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃ 
Physical property value 0.42~0.50 35~40 30~45 340~400 30~35 300000 cycles without cracks
Physical properties 300000 times no crack 
◎This physical property data was obtained from testing a 6mm thick test piece.
  These physical data are acquired by testing a sample of 6mm thick.
◎Free foam density will vary according to the season (temperature, humidity).
  Free rise density may vary with temperature &humidity.
◎Demolding time will be prolonged as the thickness of the finished product increases.
 Demold time may be prolonged with the increase of sold thickness.  
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
 Data listed are just for reference. The detail data are subject to operation.If other request on physical properties,please contact us.
HT/F 

HT-6730/F-2180
1. Characteristics: Soft hand feeling, good moldability
2. Application: Insoles
3. Typical characteristics of PU matrix
Product name Appearance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Packaging (kg)
HT-6730 Liquid or wax-like 800~1600 1.080~1.160 18
F-2180 Liquid or wax-like 200~500 1.190~1.210 20
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-6730 60-70℃ preheating for 6~8h
F-2180 60-70℃ preheating for 8~12h
5. Molding conditions and reaction parameters
Item HT/F Material temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time (s) Rise time (s) Foam density (g/cm3) Mold temperature (℃) Demolding time (min)
Technical parameters 40~45/40~45 100/70~72 6~9 45~55 0.13~0.16 45~55 5~7
◎The addition amount of catalyst is 260±5g/18kg 
◎Water and hardener are added according to actual needs 
6. Product properties
Item Molding density (g/cm3) Hardness (Shore C) Tensile strength (kg/cm2) Elongation(%) Tear strength (kg/cm)
Physical property value 0.25~0.35 25~40 15~30 250~350 10~15
◎This physical property data was obtained from testing a 6mm thick test piece.
◎Free foam density will vary according to the season (temperature, humidity).
◎Demolding time will be prolonged as the thickness of the finished product increases.
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
HT/F 

HT-6748/F-2280
1. Characteristics: Soft hand feeling, good tear resistance
2. Application: Insoles, midsoles
3. Typical characteristics of PU matrix
Product name Appearance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Packaging (kg)
HT-6748 Liquid or wax-like 700~1200 1.080~1.160 18
F-2280 Liquid or wax-like 200~600 1.090~1.110 20
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-6748 60-70℃ preheating for 6~8h
F-2280 60-70℃ preheating for 8~12h
5. Molding conditions and reaction parameters
Item HT/F Material temperature (℃) Mixing ratio (HT+SM)/F(By weight) Cream time (s) Rise time (s) Foam density (g/cm3) Mold temperature (℃) Demolding time (min)
Technical parameters 40~45/40~45 100/73~75 6~9 45~55 0.14~0.18 45~55 5~7
◎The addition amount of catalyst is 250±5g/18kg 
◎Water and hardener are added according to actual needs 
6. Product properties
Item Molding density (g/cm3) Hardness (Shore C) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm)
Physical property value 0.35~0.40 50~60 14~30 250~350 20~26
◎This physical property data was obtained from testing a 6mm thick test piece.
◎Free foam density will vary according to the season (temperature, humidity).
◎Demolding time will be prolonged as the thickness of the finished product increases.
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
HT-5340/F-2220
1. Characteristics: Good hand feeling, low hardness, good cold resistance
2. Application: Cold-resistant soles, cemented shoes
3. Typical characteristics of PU matrix
Product name Appearance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package (kg)
HT-5340 Liquid or wax-like 400~1200 1.170~1.190 18
F-2220 Liquid or wax-like 300~700 1.180~1.200 20
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-5340 60-70℃ preheating for 6~8h
F-2220 60-70℃ preheating for 8~12h
5. Molding conditions and reaction parameters
Item HT/F Material temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time (s) Rise time (s) Foam density (g/cm3) Mold temperature(℃) Demolding time (min)
Technical parameters 40~45/40~45 100/63.5~65.5 7~10 50~70 0.27~0.32 45~55 3~5
◎The addition amount of catalyst is 360±5g/18kg
◎Water and hardener are added according to actual needs 
6. Product properties
Item Molding density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%) Tear strength  (kg/cm) Flexing resistance test at -25℃
Physical property value 0.42~0.52 30~40 30~50 500~700 15~25 40000 cycles without cracks
◎This physical property data was obtained from testing a 6mm thick test piece.
◎Free foam density will vary according to the season (temperature, humidity).
◎Demolding time will be prolonged as the thickness of the finished product increases.
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
HT-6735/F-3210
4
Resin for Safety Shoes Resin for labor insurance shoes
HT-8850A/F-2180
HT-8950/F-2980
HT-8255/F-2561
1. Characteristics: High adhesion, good hand feeling, good cold resistance
Characteristic：
2. Application: Dual-density safety shoes and single-molding casual shoes
Application：
3. Typical characteristics of PU matrix
Product name Appearance Viscosity Density Packaging
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-8255 Liquid or wax-like 1500~2200 1.120~1.180 18
liquid or waxy solid
F-2561 Liquid or wax-like 200~500 1.190~1.210 20
liquid or waxy solid
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-8255 60-70℃ preheating for 6~8h
Preheated at 60-70℃ for 6~8h
F-2561 60-70℃ preheating for 8~12h
Preheated at 60-70℃ for 8~12h
5. Molding conditions and reaction parameters
Item Material temperature Mixing ratio Cream time Rise time Foam density Mold temperature Demolding time
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
Technical parameters 40~45/40~45 Outsole Midsole 6~10 50~60 Outsole Midsole 45~55 3~5
Parameter
100/74~76 100/79~81 0.4~0.5 0.25~0.35
◎The addition amount of Catalyst SM-2 is 250
◎Water and hardener are added according to actual needs   The adding content of water and hardener should added to the reality
Outsole: Water H2O 20±5g/18kg
Midsole: Water H2O 50±5g/18kg
6. Product properties
Item Molding density Hardness Tensile strength Elongation Tear strength Flexing resistance test
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -10℃ 
Physical property value Outsole Midsole Outsole Midsole Outsole Midsole Outsole Midsole Midsole 50000 cycles without cracks
Physical properties 0.8~1.0 0.45~0.65 55~75 40~60 >80 >45 350~450 300~400 >20 50000 times no crack 
◎This physical property data was obtained from testing a 6mm thick test piece.
  These physical data are acquired by testing a sample of 6mm thick.
◎Free foam density will vary according to the season (temperature, humidity).
  Free rise density may vary with temperature &humidity.
◎Demolding time will be prolonged as the thickness of the finished product increases.
 Demold time may be prolonged with the increase of sold thickness.  
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
 Data listed are just for reference。 The detail data are subject to operation.If other request on physical properties,please contact us.
HT-8801G/F-2580G
1. Characteristics: High adhesion, good cold resistance, bright surface
Characteristic：
2. Application: Cold-resistant safety shoes and single-molding casual shoes
Application：
3. Typical characteristics of PU matrix
Product name Appearance Viscosity Density Packaging
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-8801G Liquid or wax-like 1000~1800 1.116~1.124 18
liquid or waxy solid
F-2580G Liquid or wax-like 300~700 1.180~1.200 20
liquid or waxy solid
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-8801G F-2580G
60-70℃ preheating for 6~8h 60-70℃ preheating for 8~12h
Preheated at 60-70℃ for 6~8h Preheated at 60-70℃ for 8~12h
5. Molding conditions and reaction parameters
Item Material temperature Mixing ratio Cream time Rise time Foam density Mold temperature Demolding time
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
Technical parameters 40~45/40~45 Outsole Midsole 6~10 35~50 Outsole Midsole 45~55 3~5
Parameter
100/74~76 100/81~83 0.45~0.55 0.23~0.33
◎The addition amount of Catalyst SM-2 is 300
◎Water and hardener are added according to actual needs   The adding content of water and hardener should added to the reality
Outsole: Water H2O 20±5g/18kg
Midsole: Water H2O 80±5g/18kg
6. Product properties
Item Molding density Hardness Tensile strength Elongation Tear strength Flexing resistance test
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -20℃ 
Physical property value Outsole Midsole Outsole Midsole Outsole Midsole Outsole Midsole Midsole 50000 cycles without cracks
Physical properties 0.8~1.0 0.45~0.65 60~75 50~65 76~85 42~51 380~460 300~400 30~35 50000 times no crack 
◎This physical property data was obtained from testing a 6mm thick test piece.
  These physical data are acquired by testing a sample of 6mm thick.
◎Free foam density will vary according to the season (temperature, humidity).
  Free rise density may vary with temperature &humidity.
◎Demolding time will be prolonged as the thickness of the finished product increases.
 Demold time may be prolonged with the increase of sold thickness.  
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
 Data listed are just for reference。 The detail data are subject to operation.If other request on physical properties,please contact us.
5
Coldtolerant Polyester Coldtolerant polyester
HT-8840/F-2240
HT-5930G/F-2120
HT-2004/F-2580
1. Characteristics: Medium hardness, good hand feeling, good cold resistance
Characteristic：
2. Application: Cold-resistant soles
Application：
3. Typical characteristics of PU matrix
Product name Appearance Viscosity Density Package
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-2004 Liquid or wax-like 2000~2800 1.150~1.170 18
liquid or waxy solid
F-2580 Liquid or wax-like 300~700 1.180~1.200 20
liquid or waxy solid
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-2004 60-70℃ preheating for 6~8h
Preheated at 60-70℃ for 6~8h
F-2580 60-70℃ preheating for 8~12h
Preheated at 60-70℃ for 8~12h
5. Molding conditions and reaction parameters
Item Material temperature Mixing ratio Cream time Rise time Foam density Mold temperature Demolding time
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
Technical parameters 40~45/40~45 100/94~95 7~10 50~60 0.27~0.31 45~55 3~5
Parameter
◎The addition amount of Catalyst SM-2 is 220±5g/18kg
◎Water and hardener are added according to actual needs   The adding content of water and hardener should added to the reality
6. Product properties
Item Molding density Hardness Tensile strength Elongation Tear strength Flexing resistance test
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -20℃
Physical property value 0.60~0.65 57~62 38~45 460~530 33~38 50000 cycles without cracks
Physical properties 50000 times no crack
◎This physical property data was obtained from testing a 6mm thick test piece.
  These physical data are acquired by testing a sample of 6mm thick.
◎Free foam density will vary according to the season (temperature, humidity).
  Free rise density may vary with temperature &humidity.
◎Demolding time will be prolonged as the thickness of the finished product increases.
 Demold time may be prolonged with the increase of sold thickness.  
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
 Data listed are just for reference。 The detail data are subject to operation.If other request on physical properties,please contact us.
6
Transparent Material Transparent material
HT-2005/F-2580
1. Characteristics: Medium hardness, transparent material
Characteristic：
2. Application: Transparent soles
Application：
3. Typical characteristics of PU matrix
Product name Appearance Viscosity Density Package
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-2005 Liquid or wax-like 1000~1600 1.150~1.170 18
liquid or waxy solid
F-2580 Liquid or wax-like 300~700 1.180~1.200 20
liquid or waxy solid
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-2005 60-70℃ preheating for 6~8h
Preheated at 60-70℃ for 6~8h
F-2580 60-70℃ preheating for 8~12h
Preheated at 60-70℃ for 8~12h
5. Molding conditions and reaction parameters
Item Material temperature Mixing ratio Cream time Rise time Foam density Mold temperature Demolding time
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
Technical parameters 40~45/40~45 100/76~78 　 　 0.9~1.2 45~55 5~7
Parameter
◎The addition amount of Catalyst SM-2 is 300±5g/18kg
◎Water and hardener are added according to actual needs   The adding content of water and hardener should added to the reality
6. Product properties
Item Molding density Hardness Tensile strength Elongation Tear strength Flexing resistance test
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -10℃
Physical property value 0.90~1.2 57~65 80~90 550~700 55~70 50000 cycles without cracks
Physical properties 50000 times no crack
◎This physical property data was obtained from testing a 6mm thick test piece.
  These physical data are acquired by testing a sample of 6mm thick.
◎Free foam density will vary according to the season (temperature, humidity).
  Free rise density may vary with temperature &humidity.
◎Demolding time will be prolonged as the thickness of the finished product increases.
 Demold time may be prolonged with the increase of sold thickness.  
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
 Data listed are just for reference。 The detail data are subject to operation.If other request on physical properties,please contact us.
7
Polyether Polyether
HT-4460/F-4200
1. Characteristics: Excellent weather resistance, good low temperature flexibility
Characteristic：
2. Application: Outsoles
Application：
3. Typical characteristics of PU matrix
Product name Appearance Viscosity Density Package
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-4460 Liquid or wax-like 300~700 1.000~1.040 18
liquid or waxy solid
F-4200 Liquid or wax-like 200~600 1.001~1.005 20
liquid or waxy solid
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-4460 60-70℃ preheating for 6~8h
Preheated at 60-70℃ for 6~8h
F-4200 60-70℃ preheating for 8~12h
Preheated at 60-70℃ for 8~12h
5. Molding conditions and reaction parameters
Item Material temperature Mixing ratio Cream time Rise time Foam density Mold temperature Demolding time
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
Technical parameters 40~45/40~45 100/65~67 7~10 35~50 0.30~0.35 45~55 3~5
Parameter
◎The addition amount of Catalyst SM-2 catalyst is 400±5g/18kg
◎Water and hardener are added according to actual needs   The adding content of water and hardener should added to the reality
6. Product properties
Item Molding density Hardness Tensile strength Elongation Tear strength Flexing resistance test
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -40℃
Physical property value 0.60~0.70 55~65 45~55 450~550 15~20 50000 cycles without cracks
Physical properties 50000 times no crack
◎This physical property data was obtained from testing a 6mm thick test piece.
  These physical data are acquired by testing a sample of 6mm thick.
◎Free foam density will vary according to the season (temperature, humidity).
  Free rise density may vary with temperature &humidity.
◎Demolding time will be prolonged as the thickness of the finished product increases.
 Demold time may be prolonged with the increase of sold thickness.  
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
 Data listed are just for reference。 The detail data are subject to operation.If other request on physical properties,please contact us.
HT-4465/F-4230
1. Characteristics: Good low temperature flexibility, anti-slip
Characteristic：
2. Application: Outsoles
Application：
3. Typical characteristics of PU matrix
Product name Appearance Viscosity Density Package
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-4465 Liquid or wax-like 300~700 1.000~1.040 18
liquid or waxy solid
F-4230 Liquid or wax-like 200~600 1.001~1.005 20
liquid or waxy solid
◎Ideal storage temperature for materials: below 25°C
4. Material preheating
HT-4465 60-70℃ preheating for 6~8h
Preheated at 60-70℃ for 6~8h
F-4230 60-70℃ preheating for 8~12h
Preheated at 60-70℃ for 8~12h
5. Molding conditions and reaction parameters
Item Material temperature Mixing ratio Cream time Rise time Foam density Mold temperature Demolding time
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
Technical parameters 40~45/40~45 100/53~55 7~10 40~50 0.70~0.75 45~55 3~5
Parameter
◎The adding content of Catalyst SM-2 is 340±5g/18kg
◎Water and hardener are added according to actual needs   The adding content of water and hardener should added to the reality
6. Product properties
Item Molding density Hardness Tensile strength Elongation Tear strength Flexing resistance test
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -40℃
　 　 　 　 　 　 　
Physical property value 0.80~1.10 60~65 30~35 350~400 12~16 50000 cycles without cracks
Physical properties 50000 times no crack
◎This physical property data was obtained from testing a 6mm thick test piece.
  These physical data are acquired by testing a sample of 6mm thick.
◎Free foam density will vary according to the season (temperature, humidity).
  Free rise density may vary with temperature &humidity.
◎Demolding time will be prolonged as the thickness of the finished product increases.
 Demold time may be prolonged with the increase of sold thickness.  
◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us.
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.