| Download Information |
| High Hardness Polyester |
| HT-5890T/F-2280 |
| 1. Characteristic：High hardness with medium-low density | |||||||||||||||||
| 2. Application: High-heel soles and platform soles | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5890T | liquid or waxy solid | 600~1000 | 1.160~1.180 | 18 | |||||||||||||
| F-2280 | liquid or waxy solid | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-5890T | 60-70℃ preheating for 6~8h | ||||||||||||||||
| F-2280 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| 5. Processing & Reaction Parameters | |||||||||||||||||
| Item | Material temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Foam density (g/cm3) | Mold temperature(℃) | Demolding time(min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/116~118 | 7~10 | 40~60 | 0.24~0.27 | 45~55 | 3~5 | ||||||||||
| ◎The addition amount of Catalyst SM-2 is 250±5g/18kg | |||||||||||||||||
| ◎Water and hardener added as required | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | Flexing resistance test at 23℃ | |||||||||||
| Physical property value | 0.50~0.65 | 80~90 | 50~58 | 320~400 | 32~37 | 300,000 cycles without cracks | |||||||||||
| ◎Tested on 6mm-thick samples. | |||||||||||||||||
| ◎Free foam density may vary with temperature & humidity. | |||||||||||||||||
| ◎ Demolding time increases with product thickness. | |||||||||||||||||
| ◎Data provided are for reference only. Detailed specifications are subject to actual operating conditions. For additional physical property requirements, please contact us. | |||||||||||||||||
| HT-5885B/F-2260 |
| 1. Characteristics: High hardness, medium-low density | |||||||||||||||||
| 2. Application: Standing heel sole, high wedge heel | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package (kg) | |||||||||||||
| HT-5885B | Liquid or wax-like | 600~1000 | 1.160~1.180 | 18 | |||||||||||||
| F-2260 | Liquid or wax-like | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-5885B | 60-70℃ preheating for 6~8h | ||||||||||||||||
| F-2260 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | Material temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time (s) | Rise time (s) | Foam density (g/cm3) | Mold temperature(℃) | Demolding time (min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/135~137 | 6~9 | 30~38 | 0.20~0.23 | 45~55 | 3~5 | ||||||||||
| ◎The addition amount of Catalyst SM-2 is 250±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density(g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation (%) | Tear strength (kg/cm) | Flexing resistance test at 23℃ | |||||||||||
| Physical property value | 0.40~0.45 | 85~92 | 50~63 | 320~400 | 30~35 | 300,000 cycles without cracks | |||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| Medium Hardness Polyester |
| HT-5606/F-2180 |
| 1. Characteristics: bright surface, soft hand feeling | |||||||||||||||||
| 2. Application: Leather shoes, sandals | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package (kg) | |||||||||||||
| HT-5606 | Liquid or wax-like | 800~1200 | 1.120~1.200 | 18 | |||||||||||||
| F-2180 | Liquid or wax-like | 200~600 | 1.190~1.210 | 20 | |||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-5606 | 60-70℃ preheating for 6~8h | ||||||||||||||||
| F-2180 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | Material temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time (s) | Rise time (s) | Foam density (g/cm3) | Mold temperature(℃) | Demolding time(min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/99~101 | 7~10 | 50~60 | 0.23~0.30 | 45~55 | 3~5 | ||||||||||
| ◎The addition amount of Catalyst SM-2 is 240±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation (%) | Tear strength (kg/cm) | Flexing resistance test at 23℃ | |||||||||||
| Physical property value | 0.55~0.65 | 58~65 | 50~57 | 370~450 | 33~40 | 300,000 cycles without cracks | |||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| HT-5608B/F-2180 |
| 1. Characteristics: medium density, good moldability | |||||||||||||||||
| 2. Application: Casual shoes, sandals | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package (kg) | |||||||||||||
| HT-5608B | Liquid or wax-like | 500~900 | 1.160~1.180 | 18 | |||||||||||||
| F-2180 | Liquid or wax-like | 200~600 | 1.190~1.210 | 20 | |||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-5608B | 60-70℃ preheating for 6~8h | ||||||||||||||||
| F-2180 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | Material temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time (s) | Rise time (s) | Foam density (g/cm3) | Mold temperature(℃) | Demolding time (min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/116~118 | 9~11 | 40~60 | 0.22~0.25 | 45~55 | 3~5 | ||||||||||
| ◎The addition amount of Catalyst SM-2 is 270±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation (%) | Tear strength (kg/cm) | Flexing resistance test at 23℃ | |||||||||||
| Physical property value | 0.46~0.55 | 60~65 | 48~55 | 350~450 | 32~37 | 300,000 cycles without cracks | |||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| HT-5650/F-2280 |
| 1. Characteristics: Good moldability, lightweight | |||||||||||||||||
| 2. Application: Women's shoes, casual shoes | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Packaging (kg) | |||||||||||||
| HT-5650 | Liquid or wax-like | 800~1200 | 1.160~1.180 | 18 | |||||||||||||
| F-2280 | Liquid or wax-like | 200~600 | 1.180~1.200 | 20 | |||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-5650 | 60-70℃ preheating for 6~8h | ||||||||||||||||
| F-2280 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | HT/F Material temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time (s) | Rise time (s) | Foam density (g/cm3) | Mold temperature(℃) | Demolding time(min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/84.5~86.5 | 7~10 | 30~40 | 0.22~0.26 | 45~55 | 3~5 | ||||||||||
| ◎The addition amount of Catalyst SM-2 is 300±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs | |||||||||||||||||
| Water H2O 35±5g/18kg | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation (%) | Tear strength (kg/cm) | Flexing resistance test at 23℃ | |||||||||||
| Physical property value | 0.45~0.55 | 58~65 | 45~60 | 370~470 | 30~35 | 300000 times without cracks | |||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| Soft Polyester |
| HT-5830L/F-2580L |
| 1. Characteristics: low hardness, good hand feeling, cold resistance | |||||||||||||||||
| 2. Application: Cemented shoes and casual shoe soles | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package (kg) | |||||||||||||
| HT-5830L | Liquid or wax-like | 800~1200 | 1.170~1.190 | 18 | |||||||||||||
| F-2580L | Liquid or wax-like | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-5830L | 60-70℃ preheating for 6~8h | ||||||||||||||||
| F-2580L | 60-70℃ preheating for 8~12h | ||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | HT/F Material temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time (s) | Rise time (s) | Foam density (g/cm3) | Mold temperature(℃) | Demolding time (min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/54.5~56.5 | 7~10 | 40~60 | 0.21~0.25 | 45~55 | 3~5 | ||||||||||
| ◎The addition amount of Catalyst SM-2 is 300±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation (%) | Tear strength (kg/cm) | Flexing resistance test at -20℃ | |||||||||||
| Physical property value | 0.42~0.50 | 30~40 | 30~50 | 500~700 | 15~25 | 40000 cycles without cracks | |||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| HT-5835/F-2280 |
| 1. Characteristics: low hardness, good hand feeling, hydrolysis resistance | |||||||||||||||||
| 2. Application: Cemented shoes and casual shoes | |||||||||||||||||
| 3. Typical characteristis of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Packaging (kg) | |||||||||||||
| HT-5835 | Liquid or wax-like | 1000~1800 | 1.110~1.130 | 18 | |||||||||||||
| F-2280 | Liquid or wax-like | 200~600 | 1.180~1.200 | 20 | |||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-5835 | 60-70℃ preheating for 6-8h | ||||||||||||||||
| F-2280 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | HT/F Material temperature (℃) |
Mixing ratio (HT+SM)/F(By weight) | Cream time (s) | Rise time (s) | Foam density (g/cm3) | Mold temperature(℃) | Demolding time (min) | ||||||||||
| Technical parameters/td> | 40~45/40~45 | 100/62~64 | 7~10 | 40~60 | 0.21~0.25 | 45~55 | 3~5 | ||||||||||
| ◎The addition amount of Catalyst SM-2 is 350 | |||||||||||||||||
| ◎Water and hardener are added according to actual needs | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density | Hardness | Tensile strength | Elongation | Tear strength | Flexing endurance test | |||||||||||
| Items | Molded density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | Flexing Endurance Test at 23℃ | |||||||||||
| Physical property value | 0.42~0.50 | 35~40 | 30~45 | 340~400 | 30~35 | 300000 cycles without cracks | |||||||||||
| Physical properties | 300000 times no crack | ||||||||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| Data listed are just for reference. The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT/F |
| HT-6730/F-2180 |
| 1. Characteristics: Soft hand feeling, good moldability | |||||||||||||||||
| 2. Application: Insoles | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Packaging (kg) | |||||||||||||
| HT-6730 | Liquid or wax-like | 800~1600 | 1.080~1.160 | 18 | |||||||||||||
| F-2180 | Liquid or wax-like | 200~500 | 1.190~1.210 | 20 | |||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-6730 | 60-70℃ preheating for 6~8h | ||||||||||||||||
| F-2180 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | HT/F Material temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time (s) | Rise time (s) | Foam density (g/cm3) | Mold temperature (℃) | Demolding time (min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/70~72 | 6~9 | 45~55 | 0.13~0.16 | 45~55 | 5~7 | ||||||||||
| ◎The addition amount of catalyst is 260±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density (g/cm3) | Hardness (Shore C) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | ||||||||||||
| Physical property value | 0.25~0.35 | 25~40 | 15~30 | 250~350 | 10~15 | ||||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| HT/F |
| HT-6748/F-2280 |
| 1. Characteristics: Soft hand feeling, good tear resistance | |||||||||||||||||
| 2. Application: Insoles, midsoles | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Packaging (kg) | |||||||||||||
| HT-6748 | Liquid or wax-like | 700~1200 | 1.080~1.160 | 18 | |||||||||||||
| F-2280 | Liquid or wax-like | 200~600 | 1.090~1.110 | 20 | |||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-6748 | 60-70℃ preheating for 6~8h | ||||||||||||||||
| F-2280 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | HT/F Material temperature (℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time (s) | Rise time (s) | Foam density (g/cm3) | Mold temperature (℃) | Demolding time (min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/73~75 | 6~9 | 45~55 | 0.14~0.18 | 45~55 | 5~7 | ||||||||||
| ◎The addition amount of catalyst is 250±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density (g/cm3) | Hardness (Shore C) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | ||||||||||||
| Physical property value | 0.35~0.40 | 50~60 | 14~30 | 250~350 | 20~26 | ||||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| HT-5340/F-2220 |
| 1. Characteristics: Good hand feeling, low hardness, good cold resistance | |||||||||||||||||
| 2. Application: Cold-resistant soles, cemented shoes | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package (kg) | |||||||||||||
| HT-5340 | Liquid or wax-like | 400~1200 | 1.170~1.190 | 18 | |||||||||||||
| F-2220 | Liquid or wax-like | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-5340 | 60-70℃ preheating for 6~8h | ||||||||||||||||
| F-2220 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | HT/F Material temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time (s) | Rise time (s) | Foam density (g/cm3) | Mold temperature(℃) | Demolding time (min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/63.5~65.5 | 7~10 | 50~70 | 0.27~0.32 | 45~55 | 3~5 | ||||||||||
| ◎The addition amount of catalyst is 360±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | Flexing resistance test at -25℃ | |||||||||||
| Physical property value | 0.42~0.52 | 30~40 | 30~50 | 500~700 | 15~25 | 40000 cycles without cracks | |||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| HT-6735/F-3210 |
| Resin for Safety Shoes |
| HT-8850A/F-2180 |
| HT-8950/F-2980 |
| HT-8255/F-2561 |
| 1. Characteristics: High adhesion, good hand feeling, good cold resistance | |||||||||||||||||||
| Characteristic： | |||||||||||||||||||
| 2. Application: Dual-density safety shoes and single-molding casual shoes | |||||||||||||||||||
| Application： | |||||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||||
| Product name | Appearance | Viscosity | Density | Packaging | |||||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||||
| HT-8255 | Liquid or wax-like | 1500~2200 | 1.120~1.180 | 18 | |||||||||||||||
| liquid or waxy solid | |||||||||||||||||||
| F-2561 | Liquid or wax-like | 200~500 | 1.190~1.210 | 20 | |||||||||||||||
| liquid or waxy solid | |||||||||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||||
| 4. Material preheating | |||||||||||||||||||
| HT-8255 | 60-70℃ preheating for 6~8h | ||||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||||
| F-2561 | 60-70℃ preheating for 8~12h | ||||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||||
| Item | Material temperature | Mixing ratio | Cream time | Rise time | Foam density | Mold temperature | Demolding time | ||||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||||
| Technical parameters | 40~45/40~45 | Outsole | Midsole | 6~10 | 50~60 | Outsole | Midsole | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||||
| 100/74~76 | 100/79~81 | 0.4~0.5 | 0.25~0.35 | ||||||||||||||||
| ◎The addition amount of Catalyst SM-2 is 250 | |||||||||||||||||||
| ◎Water and hardener are added according to actual needs The adding content of water and hardener should added to the reality | |||||||||||||||||||
| Outsole: Water H2O 20±5g/18kg | |||||||||||||||||||
| Midsole: Water H2O 50±5g/18kg | |||||||||||||||||||
| 6. Product properties | |||||||||||||||||||
| Item | Molding density | Hardness | Tensile strength | Elongation | Tear strength | Flexing resistance test | |||||||||||||
| Items | Molded density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | Flexing Endurance Test at -10℃ | |||||||||||||
| Physical property value | Outsole | Midsole | Outsole | Midsole | Outsole | Midsole | Outsole | Midsole | Midsole | 50000 cycles without cracks | |||||||||
| Physical properties | 0.8~1.0 | 0.45~0.65 | 55~75 | 40~60 | >80 | >45 | 350~450 | 300~400 | >20 | 50000 times no crack | |||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||||
| Data listed are just for reference。 The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||||
| HT-8801G/F-2580G |
| 1. Characteristics: High adhesion, good cold resistance, bright surface | |||||||||||||||||||
| Characteristic： | |||||||||||||||||||
| 2. Application: Cold-resistant safety shoes and single-molding casual shoes | |||||||||||||||||||
| Application： | |||||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||||
| Product name | Appearance | Viscosity | Density | Packaging | |||||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||||
| HT-8801G | Liquid or wax-like | 1000~1800 | 1.116~1.124 | 18 | |||||||||||||||
| liquid or waxy solid | |||||||||||||||||||
| F-2580G | Liquid or wax-like | 300~700 | 1.180~1.200 | 20 | |||||||||||||||
| liquid or waxy solid | |||||||||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||||
| 4. Material preheating | |||||||||||||||||||
| HT-8801G | F-2580G | ||||||||||||||||||
| 60-70℃ preheating for 6~8h | 60-70℃ preheating for 8~12h | ||||||||||||||||||
| Preheated at 60-70℃ for 6~8h | Preheated at 60-70℃ for 8~12h | ||||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||||
| Item | Material temperature | Mixing ratio | Cream time | Rise time | Foam density | Mold temperature | Demolding time | ||||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||||
| Technical parameters | 40~45/40~45 | Outsole | Midsole | 6~10 | 35~50 | Outsole | Midsole | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||||
| 100/74~76 | 100/81~83 | 0.45~0.55 | 0.23~0.33 | ||||||||||||||||
| ◎The addition amount of Catalyst SM-2 is 300 | |||||||||||||||||||
| ◎Water and hardener are added according to actual needs The adding content of water and hardener should added to the reality | |||||||||||||||||||
| Outsole: Water H2O 20±5g/18kg | |||||||||||||||||||
| Midsole: Water H2O 80±5g/18kg | |||||||||||||||||||
| 6. Product properties | |||||||||||||||||||
| Item | Molding density | Hardness | Tensile strength | Elongation | Tear strength | Flexing resistance test | |||||||||||||
| Items | Molded density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | Flexing Endurance Test at -20℃ | |||||||||||||
| Physical property value | Outsole | Midsole | Outsole | Midsole | Outsole | Midsole | Outsole | Midsole | Midsole | 50000 cycles without cracks | |||||||||
| Physical properties | 0.8~1.0 | 0.45~0.65 | 60~75 | 50~65 | 76~85 | 42~51 | 380~460 | 300~400 | 30~35 | 50000 times no crack | |||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||||
| Data listed are just for reference。 The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||||
| Coldtolerant Polyester |
| HT-8840/F-2240 |
| HT-5930G/F-2120 |
| HT-2004/F-2580 |
| 1. Characteristics: Medium hardness, good hand feeling, good cold resistance | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2. Application: Cold-resistant soles | |||||||||||||||||
| Application： | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity | Density | Package | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-2004 | Liquid or wax-like | 2000~2800 | 1.150~1.170 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2580 | Liquid or wax-like | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-2004 | 60-70℃ preheating for 6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2580 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | Material temperature | Mixing ratio | Cream time | Rise time | Foam density | Mold temperature | Demolding time | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/94~95 | 7~10 | 50~60 | 0.27~0.31 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎The addition amount of Catalyst SM-2 is 220±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density | Hardness | Tensile strength | Elongation | Tear strength | Flexing resistance test | |||||||||||
| Items | Molded density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | Flexing Endurance Test at -20℃ | |||||||||||
| Physical property value | 0.60~0.65 | 57~62 | 38~45 | 460~530 | 33~38 | 50000 cycles without cracks | |||||||||||
| Physical properties | 50000 times no crack | ||||||||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| Data listed are just for reference。 The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| Transparent Material |
| HT-2005/F-2580 |
| 1. Characteristics: Medium hardness, transparent material | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2. Application: Transparent soles | |||||||||||||||||
| Application： | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity | Density | Package | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-2005 | Liquid or wax-like | 1000~1600 | 1.150~1.170 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2580 | Liquid or wax-like | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-2005 | 60-70℃ preheating for 6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2580 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | Material temperature | Mixing ratio | Cream time | Rise time | Foam density | Mold temperature | Demolding time | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/76~78 | 0.9~1.2 | 45~55 | 5~7 | ||||||||||||
| Parameter | |||||||||||||||||
| ◎The addition amount of Catalyst SM-2 is 300±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density | Hardness | Tensile strength | Elongation | Tear strength | Flexing resistance test | |||||||||||
| Items | Molded density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | Flexing Endurance Test at -10℃ | |||||||||||
| Physical property value | 0.90~1.2 | 57~65 | 80~90 | 550~700 | 55~70 | 50000 cycles without cracks | |||||||||||
| Physical properties | 50000 times no crack | ||||||||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| Data listed are just for reference。 The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| Polyether |
| HT-4460/F-4200 |
| 1. Characteristics: Excellent weather resistance, good low temperature flexibility | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2. Application: Outsoles | |||||||||||||||||
| Application： | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity | Density | Package | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-4460 | Liquid or wax-like | 300~700 | 1.000~1.040 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-4200 | Liquid or wax-like | 200~600 | 1.001~1.005 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-4460 | 60-70℃ preheating for 6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-4200 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | Material temperature | Mixing ratio | Cream time | Rise time | Foam density | Mold temperature | Demolding time | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/65~67 | 7~10 | 35~50 | 0.30~0.35 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎The addition amount of Catalyst SM-2 catalyst is 400±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density | Hardness | Tensile strength | Elongation | Tear strength | Flexing resistance test | |||||||||||
| Items | Molded density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | Flexing Endurance Test at -40℃ | |||||||||||
| Physical property value | 0.60~0.70 | 55~65 | 45~55 | 450~550 | 15~20 | 50000 cycles without cracks | |||||||||||
| Physical properties | 50000 times no crack | ||||||||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| Data listed are just for reference。 The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-4465/F-4230 |
| 1. Characteristics: Good low temperature flexibility, anti-slip | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2. Application: Outsoles | |||||||||||||||||
| Application： | |||||||||||||||||
| 3. Typical characteristics of PU matrix | |||||||||||||||||
| Product name | Appearance | Viscosity | Density | Package | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-4465 | Liquid or wax-like | 300~700 | 1.000~1.040 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-4230 | Liquid or wax-like | 200~600 | 1.001~1.005 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎Ideal storage temperature for materials: below 25°C | |||||||||||||||||
| 4. Material preheating | |||||||||||||||||
| HT-4465 | 60-70℃ preheating for 6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-4230 | 60-70℃ preheating for 8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5. Molding conditions and reaction parameters | |||||||||||||||||
| Item | Material temperature | Mixing ratio | Cream time | Rise time | Foam density | Mold temperature | Demolding time | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| Technical parameters | 40~45/40~45 | 100/53~55 | 7~10 | 40~50 | 0.70~0.75 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎The adding content of Catalyst SM-2 is 340±5g/18kg | |||||||||||||||||
| ◎Water and hardener are added according to actual needs The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6. Product properties | |||||||||||||||||
| Item | Molding density | Hardness | Tensile strength | Elongation | Tear strength | Flexing resistance test | |||||||||||
| Items | Molded density (g/cm3) | Hardness (Shore A) | Tensile strength (kg/cm2) | Elongation(%) | Tear strength (kg/cm) | Flexing Endurance Test at -40℃ | |||||||||||
| Physical property value | 0.80~1.10 | 60~65 | 30~35 | 350~400 | 12~16 | 50000 cycles without cracks | |||||||||||
| Physical properties | 50000 times no crack | ||||||||||||||||
| ◎This physical property data was obtained from testing a 6mm thick test piece. | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎Free foam density will vary according to the season (temperature, humidity). | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎Demolding time will be prolonged as the thickness of the finished product increases. | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎The above data is for reference only, and the specific data is subject to actual operation. If other physical property indicators are required, please contact us. | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
2
Jiangsu Huada
xysz
| Download Information |
| PU Resin For Shoe Soles |
| HT-5516/F-2567 |
| 1. Characteristics: Medium-low hardness, medium-low density, fast demolding, good moldability. | ||||||
| 2. Application: Cloth shoes, cotton shoes, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-5516 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=30/24 (barrel) |
| F-2567 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5516 | SM-11 | Water | Hardener | ||
| Ratio | 18Kg | 350~380g | 50~70g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/86~90 | Sole molding density | 0.47-0.52 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 38-45 | ||
| B: 40-42 | ASKER-C | / | ||||
| Cream time (s) | 3~6 | Tensile strength (MPa) | ≥ 3.0 | |||
| Rise time (s) | 9~22 | Elongation (％) | ≥ 400 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥ 20.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.22~0.26 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~4 | Flexing resistance test (times) | 30000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-5516 at 50-60℃ for 10±2 hours; F-2567 at 50-70℃ for 20±4 hours. | ||||||
| ● The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ● The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5516/F-2618 |
| 1. Characteristics: Medium-low hardness, medium-low density, fast demolding, good moldability. | ||||||
| 2. Application: Cloth shoes, cotton shoes, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-5516 | Liquid or wax-like | 1205±100 | 1.02~1.10 | 18 | 6 months | A/B=32/29 (barrel) |
| F-2618 | Liquid or wax-like | 200±50 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5516 | SM-11 | Water | Hardener | ||
| Ratio | 18Kg | 280~350g | 50~75g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/73~75 | Sole molding density | 0.42~0.5 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 45~55 | ||
| B: 40-42 | ASKER-C | / | ||||
| Cream time (s) | 3~6 | Tensile strength (MPa) | ≥ 3.0 | |||
| Rise time (s) | 9~22 | Elongation (％) | ≥ 400 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥ 20.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.21~0.25 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~4 | Flexing resistance test (times) | 50000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-5516 at 50-60℃ for 10±2 hours; F-2618 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5518/F-2567 |
| 1. Characteristics: Medium hardness, medium-low density, fast demolding, good moldability. | ||||||
| 2. Application: Cloth shoes, cotton shoes, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-5518 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=28/25 (barrel) |
| F-2567 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5518 | SM-11 | Water | Hardener | ||
| Ratio | 18Kg | 350~380g | 50~70g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/93~97 | Sole molding density | 0.47-0.52 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 45-52 | ||
| B: 40-42 | ASKER-C | / | ||||
| Cream time (s) | 4~5 | Tensile strength (MPa) | ≥ 3.0 | |||
| Rise time (s) | 9~22 | Elongation (％) | ≥ 400 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥ 20.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.22~0.26 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~4 | Flexing resistance test (times) | 30000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-5518 at 50-60℃ for 10±2 hours; F-2567 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5526/F-2560 |
| 1. Characteristics: Medium-low hardness, medium-low density, lightweight, good moldability. | ||||||
| 2. Application: Cloth shoes, cotton shoes, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-5526 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=32/21 (barrel) |
| F-2560 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5526 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 320~350g | 80~90g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/73~77 | Sole molding density | 0.48-0.55 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 35-50 | ||
| B: 40-42 | ASKER-C | / | ||||
| Cream time (s) | 5~8 | Tensile strength (MPa) | ≥ 5.0 | |||
| Rise time (s) | 9~22 | Elongation (％) | ≥ 350 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥ 20.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.22~0.26 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~4 | Flexing resistance test (times) | 30000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-5526 at 50-60℃ for 10±2 hours; F-2560 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5526/F-2567 |
| 1. Characteristics: Medium-low hardness, medium-low density, fast demolding, good moldability. | ||||||
| 2. Application: Women's shoes, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-5526 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=32/21 (barrel) |
| F-2567 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5526 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 300-350g | 80~100g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/70~75 | Sole molding density | 0.48-0.55 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 35-45 | ||
| B: 40-42 | ASKER-C | / | ||||
| Cream time (s) | 5~8 | Tensile strength (MPa) | ≥5.0 | |||
| Rise time (s) | 9~22 | Elongation (％) | ≥ 350 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥ 20.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.26~0.27 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~4 | Flexing resistance test (times) | 30000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-5526 at 50-60℃ for 10±2 hours; F-2567 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5528/F-2560 |
| 1. Characteristics: Medium-low hardness, medium-low density, fast demolding, good moldability. | ||||||
| 2. Application: Cloth shoes, cotton shoes, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-5528 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=30/23 (barrel) |
| F-2560 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5528 | SM-16 | Water | Hardener | ||
| Ratio | 18Kg | 320~350g | 80~90g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/80~85 | Sole molding density | 0.48-0.55 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 45-52 | ||
| B: 40-42 | ASKER-C | / | ||||
| Cream time (s) | 5~8 | Tensile strength (MPa) | ≥ 6.5 | |||
| Rise time (s) | 9~22 | Elongation (％) | ≥ 400 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥ 20.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.22~0.26 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 3~4 | Flexing resistance test (times) | 30000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-5528 at 50-60℃ for 10±2 hours; F-2560 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| Ordinary Resin For Shoe Soles |
| HT-5650/F-2619 |
| 1. Characteristics: Medium-low hardness, good moldability. | ||||||
| 2. Application: Casual shoes, sandals, leather shoe soles, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-5650 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=28/25 (barrel) |
| F-2619 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5650 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 240~260g | 5~10g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mmthick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/87~89 | Sole molding density | 0.5-0.55 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 38-42 | Hardness | JISA | 55-65 | ||
| B: 38-42 | ASKER-C | / | ||||
| Cream time (s) | 7~9 | Tensile strengthMPa) | ≥ 4.0 | |||
| Rise time (s) | 10~25 | Elongation (％) | ≥ 300 | |||
| Tack-free time (s) | 35~40 | Tear strength (kN/m) | ≥20 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.23~0.26 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 3~5 | Flexing resistance test (times) | 30000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-5650 at 50-60℃ for 10±2 hours; F-2619 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5655/F-2618 |
| Characteristics: good moldability, lightweight. | ||||||
| Application: Women's shoes, protective shoes. | ||||||
| 1. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-5655 | Liquid or wax-like | 900±100 | 1.02~1.10 | 18 | 6 months | A/B=30/27 (barrel) |
| F-2618 | Liquid or wax-like | 200±50 | 1.18~1.20 | 20 | 3 months | |
| 2. Catalyst and additives: | ||||||
| Category | HT-5655 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 300~350g | 40~50g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 3. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/81~83 | Sole molding density | 0.47-0.52 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 56-65 | ||
| B: 40-42 | ASKER-C | / | ||||
| Cream time (s) | 3~6 | Tensile strength (MPa) | ≥ 3.0 | |||
| Rise time (s) | 9~22 | Elongation (％) | ≥ 400 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥ 20.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.23~0.26 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 3~4 | Flexing resistance test (times) | 50000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-5655 at 50-60℃ for 10±2 hours; F-2618 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5670/F-2618 |
| 1. Characteristics: medium hardness, good moldability. | ||||||
| 2. Application: Men's and women's sandals, leather shoes, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-5670 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=28/25 (barrel) |
| F-2618 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5670 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 280~320g | 50~70g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/96~98 | Sole molding density | 0.45-0.50 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 38-42 | Hardness | JISA | 68-74 | ||
| B: 38-42 | ASKER-C | / | ||||
| Cream time (s) | 7~9 | Tensile strength (MPa) | ≥ 4.0 | |||
| Rise time (s) | 10~25 | Elongation (％) | ≥ 300 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥ 25.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.2~0.23 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 3~5 | Flexing resistance test (times) | 40000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-5670 at 50-60℃ for 10±2 hours; F-2618 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5670/F-2619 |
| 1. Characteristics: medium hardness, good moldability. | ||||||
| 2. Application: Men's and women's sandals, leather shoes, etc. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-5670 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=28/26(Barrel) |
| F-2619 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5670 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 280~320g | 50~70g | Add appropriately according to hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick specimen) | Reference physical properties | |||
| Reference ratio (by weight) | 100/100~102 | Sole molding density | 0.45-0.50 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 38-42 | Hardness | JISA | 68-74 | ||
| B: 38-42 | ASKER-C | |||||
| Cream time (s) | 7-9 | Tensile strength (MPa) | ≥ 4.0 | |||
| Rise time (s) | 10-25 | Elongation (%) | ≥ 350 | |||
| Tack-free time (s) | 30~36 | DIN abrasion (mm³) | ≦130 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.21~0.23 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~5 | Flexing resistance test (cycles) | 40000 cycles without cracks | |||
| (min) | 23℃, bending 90° | |||||
| ● Optimal dissolving conditions: HT-5670 at 50-60℃ for 10±2 hours; F-2619 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5680/F-2619 |
| 1. Characteristics: medium-high hardness, good moldability, good hand feeling. | ||||||
| 2. Application: Men's and women's sandals, leather shoes, etc. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-5680 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=25/28(Barrel) |
| F-2619 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5680 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 280~320g | 80~90g | Add appropriately according to hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick specimen) | Reference physical properties | |||
| Reference ratio (by weight) | 100/120~122 | Sole molding density | 0.42-0.55 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 38-42 | Hardness | JISA | 75-80 | ||
| B: 38-42 | ASKER-C | / | ||||
| Cream time (s) | 5~6 | Tensile strength (MPa) | ≥ 4.5 | |||
| Rise time (s) | 10~25 | Elongation (%) | ≥ 350 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥26.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.2~0.25 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~5 | Flexing resistance test (cycles) | 30000 cycles without cracks | |||
| (min) | 23℃, bending 90° | |||||
| ● Optimal dissolving conditions: HT-5680 at 50-60℃ for 10±2 hours; F-2619 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5690/F-2619 |
| 1. Characteristics: medium-high hardness, good moldability. | ||||||
| 2. Application: Men's and women's sandals, leather shoes, etc. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-5690 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=28/25(Barrel) |
| F-2619 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5690 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 250~280g | 80~90g | Add appropriately according to hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test Item (6mm thick sample) | Reference physical property values | |||
| Reference ratio (weight ratio) | 100/128~130 | Sole molding density | 0.45-0.55 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (°C) | A: 38-42 | Hardness | JISA | 75-80 | ||
| B: 38-42 | ASKER-C | / | ||||
| Cream time (s) | 7~9 | Tensile strength (MPa) | ≥ 4.5 | |||
| Rise time (s) | 10~25 | Elongation (%) | ≥ 300 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥30.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.2~0.25 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~5 | Folding resistance test (cycles) | 30,000 cycles without cracks | |||
| (min) | 23°C, bending 90° | |||||
| ● Optimal dissolving conditions: HT-5690 at 50-60℃ for 10±2 hours; F-2619 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-5890T/F-2619 |
| 1. Characteristics: medium-high hardness, good moldability. | ||||||
| 2. Application: Men's and women's sandals, leather shoes, etc. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-5890T | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=28/25(Barrel) |
| F-2619 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5890T | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 280~300g | 10~20g | Add appropriately according to hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test Item (6mm thick sample) | Reference physical property values | |||
| Reference ratio (weight ratio) | 100/128~130 | Sole molding density | 0.5-0.55 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (°C) | A: 38-42 | Hardness | JISA | 80-85 | ||
| B: 38-42 | ASKER-C | / | ||||
| Cream time (s) | 7~9 | Tensile strength (MPa) | ≥ 5.0 | |||
| Rise time (s) | 10~25 | Elongation (%) | ≥ 300 | |||
| Tack-free time (s) | 35~40 | Tear strength (kN/m) | ≥30.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.24~0.27 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~5 | Folding resistance test (cycles) | 30,000 cycles without cracks | |||
| (min) | 23°C, bending 90° | |||||
| ● Optimal dissolving conditions: HT-5890T at 50-60℃ for 10±2 hours; F-2619 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-8810/F-2529 |
| 1. Characteristics: medium, high hardness, good moldability, good elasticity. | ||||||
| 2. Application: Wood chip soles, etc. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-8810 | Liquid or wax-like | 1600±400 | 1.02~1.10 | 18 | 6 months | A/B=35/19(Barrel) |
| F-2529 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-8810 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 220~240g | 15g | 300g | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/59~61 | Sole molding density | / | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 38-42 | Hardness | JISA | 75-80 | ||
| B: 38-42 | ASKER-C | / | ||||
| Cream time (s) | 7~9 | Tensile strength (MPa) | ≥ 5.0 | |||
| Rise time (s) | 10~45 | Elongation (%) | ≥ 450 | |||
| Tack-free time (s) | 50~55 | Tear strength (kN/m) | ≥28.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.45~0.55 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 3~5 | Flexing resistance test (times) | / | |||
| (min) | 23℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-8810 at 50-60℃ for 10±2 hours; F-2529 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| Resin For Labor Insurance Shoe |
| HT-8233/F-2563 |
| 1. Characteristics: medium hardness, transparent material. | ||||||
| 2. Application: Production of transparent and semi-transparent soles. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-8233 | Liquid or wax-like | 1000±400 | 1.02~1.10 | 18 | 6 months | A/B=35/19 (barrel) |
| F-2563 | Liquid or wax-like | 500±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-8233 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 300~350g | / | 0-200g | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/60 | Sole molding density | 1.0-1.2 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 64-67 | ||
| B: 40-42 | ASKER-C | / | ||||
| Cream time (s) | / | Tensile strength (MPa) | ≥11.0 | |||
| Rise time (s) | / | Elongation (％) | ≥ 600 | |||
| Curing time (s) | 80~85 | Tear strength (kN/m) | ≥ 30.0 | |||
| Metal mold temperature | 40~55 | DIN abrasion resistance (mm3) | 120 | |||
| (℃) | ||||||
| Demolding time | 3~5 | Flexing resistance test (times) | 50000 cycles without cracks | |||
| (min) | 25℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-8233 at 50-60℃ for 10±2 hours; F-2563 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-8255/F-2561 |
| 1. Characteristics: good adhesion, good surface skinning, low density. | ||||||
| 2. Application: Outsoles and midsoles for safety shoes and cemented shoes, industrial cushioning parts. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/50℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-8255 | Liquid or wax-like | 1700±400 | 1.12~1.20 | 18 | 6 months | A/B=31/23(Barrel) |
| F-2561 | Liquid or wax-like | 300±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-8255 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 280-300g | Outsole:/ | Add appropriately according to hardness | ||
| Midsole:30-40g | ||||||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | Outsole: 100/75-77 | Sole molding density | Outsole: 0.80-1.10 | |||
| (HT+SM)/F | Midsole: 100/80-82 | (g/cm³) | Midsole: 0.45-0.65 | |||
| Operating temperature (℃) | A: 38-42 | Hardness | JISA | Outsole: 55-75 | ||
| B: 38-42 | Midsole: 40-60 | |||||
| ASKER-C | / | |||||
| Cream time (s) | Outsole: 5~6 | Tensile strength (Mpa) | Outsole: ≥ 7.0 | |||
| Midsole: 3~4 | Midsole: ≥ 4.5 | |||||
| Rise time (s) | Outsole: 6~38 | Tear strength (kN/m) | Outsole: ≥45.0 | |||
| Midsole: 5~35 | Midsole: ≥20.0 | |||||
| Tack-free time (s) | Outsole: 48~50 | DIN abrasion (mm3) | ≤120 | |||
| Midsole: 39~41 | ||||||
| Metal mold temperature | 45~55 | Free rise density | Outsole: 0.40-0.50 | |||
| (℃) | (g/cm³) | Midsole: 0.25-0.35 | ||||
| Demoulding time | 3~5 | Flexing resistance test (pre-cut 2mm) | No cut growth after 50,000 cycles | |||
| (min) | 25℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-8255 at 60-70℃ for 10±2 hours; F-2561 at 60-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-8812/F-2530 |
| 1. Characteristics: polyester-based two-component PU foaming system, cold resistant. | ||||||
| 2. Application: Safety shoes, cemented shoes, outsoles, midsoles, industrial cushioning parts. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/50℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-8812 | Liquid or wax-like | 1500±400 | 1.12~1.20 | 18 | 6 months | A/B=32/21 (barrel) |
| F-2530 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-8812 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 300-350g | Outsole: 15g | Midsole: 500g | ||
| Midsole: 65-70g | ||||||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | Outsole: 100/49-51 | Sole molding density | Outsole: 0.80-1.10 | |||
| (HT+SM)/F | Midsole: 100/74-76 | (g/cm³) | Midsole: 0.45-0.65 | |||
| Operating temperature (℃) | A: 38-42 | Hardness | JISA | Outsole: 60-70 | ||
| B: 38-42 | Midsole: 45-52 | |||||
| ASKER-C | / | |||||
| Cream time (s) | Outsole: 6~7 | Tensile strength (MPa) | Outsole ≥ 7.0 | |||
| Midsole: 3~4 | Midsole ≥ 5.5 | |||||
| Rise time (s) | Outsole: 8~45 | Tear strength (kN/m) | Outsole ≥ 55.0 | |||
| Midsole: 5~35 | Midsole ≥ 20.0 | |||||
| Tack-free time (s) | Outsole: 40~50 | DIN abrasion resistance (mm3) | ≤105 | |||
| Midsole: 38~42 | ||||||
| Metal mold temperature | 40~55 | Free rise density | Outsole: 0.40-0.50 | |||
| (℃) | (g/cm³) | Midsole: 0.27-0.35 | ||||
| Demolding time | 3~5 | Flexing resistance test (pre-cut 2mm) | Cut growth ≤4mm | |||
| (min) | 25℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-8812 at 60-70℃ for 10±2 hours; F-2530 at 60-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-8860/F-2570 |
| 1. Characteristics: medium hardness, good moldability. | |||||||
| 2. Application: Military shoes, etc. | |||||||
| 3. Properties of PU matrix: | |||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: | |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | |||||
| HT-8860 | Liquid or wax-like | 1000±400 | 1.02~1.10 | 18 | 6 months | A/B=30/23 (barrel) | |
| F-2570 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | ||
| 4. Catalyst and additives: | |||||||
| Category | HT-8860 | SM-2 | Water | Hardener | |||
| Ratio | 18Kg | 280~320g | 80~90g | Add approximately according to the hardness | |||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | |||||||
| 5. Molding conditions and physical property value: | |||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | ||||
| Reference ratio (weight ratio) | 100/85~89 | Sole molding density | 0.55-0.60 | ||||
| (HT+SM)/F | (g/cm³) | ||||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 60-65 | |||
| B: 40-42 | ASKER-C | / | |||||
| Cream time (s) | 5~6 | Tensile strength (MPa) | ≥ 6.0 | ||||
| Rise time (s) | 7~35 | Elongation (％) | ≥ 300 | ||||
| Tack-free time (s) | 65~72 | Tear strength (kN/m) | ≥ 23.0 | ||||
| Metal mold temperature | 50~55 | Free rise density | 0.27~0.30 | ||||
| (℃) | (g/cm³) | ||||||
| Demolding time | 4~6 | Flexing resistance test (times) | 30000 cycles without cracks | ||||
| (min) | 23℃, bend 90° | ||||||
| ● Optimal dissolving conditions: HT-8860 at 50-60℃ for 10±2 hours; F-2570 at 50-70℃ for 20±4 hours. | |||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | |||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | |||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | |||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | |||||||
| Resin For Imitation-Wood |
| HT-9890/F-2390 |
| 1. Characteristics: ultra-high hardness, ultra-low density. | ||||||
| 2. Application: Women's sandals, inserted heels, waterproof platforms. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-9890 | Liquid or wax-like | 1100±400 | 1.12~1.14 | 18 | 6 months | A/B=21/32 (barrel) |
| F-2390 | Liquid or wax-like | 500±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-9890 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 250-280g | 120g | 1500g | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/165-170 | Sole molding density | 0.3-0.35 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 90-95 | ||
| B: 35-40 | ASKER-C | / | ||||
| Cream time (s) | 8~9 | Tensile strength (MPa) | ≥3.5 | |||
| Rise to top time (s) | 9~35 | Elongation (％) | ≥50 | |||
| Tack-free time (s) | 35~38 | DIN abrasion resistance (mm3) | ≦350 | |||
| Metal mold temperature | 50~60 | Free rise density | 0.16~0.17 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~5 | Flexing resistance test (times) | / | |||
| (min) | 23℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-9890 at 50-60℃ for 10±2 hours; F-2390 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| Low-density Resin |
| HT-5040/F-2330 |
| 1. Characteristics: low hardness, medium-low density, good moldability. | ||||||
| 2. Application: Midsoles, slippers, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-5040 | Liquid or wax-like | 1200±400 | 1.02~1.10 | 18 | 6 months | A/B=34/19 (barrel) |
| F-2330 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5040 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 300~330g | 70~90g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/61~63 | Sole molding density | 0.4-0.45 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 35-40 | ||
| B: 35-40 | ASKER-C | / | ||||
| Cream time (s) | 4~7 | Tensile strength (MPa) | 5.0~7.0 | |||
| Rise time (s) | 8~25 | Elongation (％) | ≥400 | |||
| Tack-free time (s) | 30~36 | DIN abrasion resistance (mm3) | / | |||
| Metal mold temperature | 53~60 | Free rise density | 0.19~0.21 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~5 | Flexing resistance test (times) | 50000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-5040 at 50-60℃ for 10±2 hours; F-2330 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-9366/F-2330 |
| 1. Characteristics: medium hardness, ultra-low density, good moldability. | ||||||
| 2. Application: Men's and women's sandals, slippers, beach shoes, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-9366 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=28/25 (barrel) |
| F-2330 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-9366 | SM-62 | Water | Hardener | ||
| Ratio | 18Kg | 270~300g | 40~60g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/102~104 | Sole molding density | 0.3-0.35 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 55-65 | ||
| B: 35-40 | ASKER-C | / | ||||
| Cream time (s) | 3~4 | Tensile strength (MPa) | ≥3.0 | |||
| Rise time (s) | 4~22 | Tear strength (kN/m) | ≥ 15.0 | |||
| Tack-free time (s) | 23~30 | DIN abrasion resistance (mm3) | ≦350 | |||
| Metal mold temperature | 50~60 | Free rise density | 0.16~0.18 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~5 | Flexing resistance test (times) | 40000 cycles without cracks | |||
| (min) | 25℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-9366 at 50-60℃ for 10±2 hours; F-2330 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-9375/F-2619 |
| 1. Characteristics: medium hardness, low density, good moldability. | ||||||
| 2. Application: Men's and women's sandals, slippers, beach shoes, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-9375 | Liquid or wax-like | 1600±400 | 1.02~1.10 | 18 | 6 months | A/B=28/25 (barrel) |
| F-2619 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-9375 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 280~300g | 40~50g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/116~118 | Sole molding density | 0.4-0.42 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 65-75 | ||
| B: 35-40 | ASKER-C | / | ||||
| Cream time (s) | 4~5 | Tensile strength (MPa) | ≥3.0 | |||
| Rise time (s) | 5~23 | Tear strength (kN/m) | ≥ 15.0 | |||
| Tack-free time (s) | 23~30 | DIN abrasion resistance (mm3) | ≦350 | |||
| Metal mold temperature | 50~60 | Free rise density | 0.16~0.18 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~5 | Flexing resistance test (times) | 40000 cycles without cracks | |||
| (min) | 25℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-9375 at 50-60℃ for 10±2 hours; F-2619 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| HT-9377/F-2618 |
| 1. Characteristics: medium-high hardness, low density, good moldability. | ||||||
| 2. Application: Women's high heels, inserted heels, waterproof platforms, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-9377 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=24/29 (barrel) |
| F-2618 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-9377 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 260~300g | 70~100g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/133~136 | Sole molding density | 0.38-0.50 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 75-85 | ||
| B: 35-40 | ASKER-C | / | ||||
| Cream time (s) | 5~8 | Tensile strength (MPa) | ≥3.0 | |||
| Rise time (s) | 9~26 | Tear strength (kN/m) | ≥15.0 | |||
| Tack-free time (s) | 32~36 | DIN abrasion resistance (mm3) | ≦350 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.18~0.21 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 4~5 | Flexing resistance test (times) | 40000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-9377 at 50-60℃ for 10±2 hours; F-2618 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-9388/F-2380 |
| 1. Characteristics: medium-high hardness, ultra-low density, good moldability. | ||||||
| 2. Application: Women's high heels, inserted heels, waterproof platforms, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-9388 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=26/30 (barrel) |
| F-2380 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-9388 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 250~280g | 70~110g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/160~164 | Sole molding density | 0.38-0.50 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 80-90 | ||
| B: 35-40 | ASKER-C | / | ||||
| Cream time (s) | 5~8 | Tensile strength (MPa) | ≥3.0 | |||
| Rise time (s) | 9~26 | Tear strength (kN/m) | ≥17.0 | |||
| Tack-free time (s) | 30~36 | DIN abrasion resistance (mm3) | ≦350 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.17~0.20 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 4~5 | Flexing resistance test (times) | 40000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-9388 at 50-60℃ for 10±2 hours; F-2380 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-9388/F-2618 |
| 1. Characteristics: medium-high hardness, ultra-low density, good moldability. | ||||||
| 2. Application: Women's high heels, inserted heels, waterproof platforms, etc. | ||||||
| 3. Properties of PU matrix: | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/barrel) | ||||
| HT-9388 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=20/31 (barrel) |
| F-2618 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-9388 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 250~280g | 70~110g | Add approximately according to the hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/168~172 | Sole molding density | 0.38-0.50 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 75-85 | ||
| B: 35-40 | ASKER-C | / | ||||
| Cream time (s) | 5~8 | Tensile strength (MPa) | ≥3.0 | |||
| Rise time (s) | 9~26 | Tear strength (kN/m) | ≥15.0 | |||
| Tack-free time (s) | 30~36 | DIN abrasion resistance (mm3) | ≦350 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.17~0.20 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 4~5 | Flexing resistance test (times) | 40000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-9388 at 50-60℃ for 10±2 hours; F-2618 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| Resin For Tire |
| HT-5670/F-2191 |
| 1. Characteristics: medium-high hardness, good moldability. | ||||||
| 2. Application: Tires, etc. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-5670 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=30/23(Barrel) |
| F-2191 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-5670 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 260~300g | 20~30g | Add appropriately according to hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/81~85 | Tire molding density | 0.45-0.48 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 38-42 | Hardness | JISA | 83-85 | ||
| B: 38-42 | ASKER-C | / | ||||
| Cream time (s) | 5~6 | Tensile strength (MPa) | ≥3.5 | |||
| Rise time (s) | 7~28 | Elongation (%) | ≥ 300 | |||
| Tack-free time (s) | 35~36 | DIN abrasion (mm3) | / | |||
| Metal mold temperature | 50~55 | Free rise density | 0.25~0.26 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 3~5 | Flexing resistance test (times) | 50000 cycles | |||
| (min) | 23℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-5670 at 50-60℃ for 10±2 hours; F-2191 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-8211/F-2530 |
| 1. Characteristics: High hardness, good moldability, good elasticity. | ||||||
| 2. Application: Tires, etc. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-8211 | Liquid or wax-like | 1600±400 | 1.02~1.10 | 18 | 6 months | A/B=25/28(Barrel) |
| F-2530 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-8211 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 200~250g | 20~30g | Add appropriately according to hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test Item (6mm thick sample) | Reference physical property values | |||
| Reference ratio (weight ratio) | 100/123~125 | Sole molding density | 0.6-0.7 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (°C) | A: 38-42 | Hardness | JISA | 85-90 | ||
| B: 38-42 | ASKER-C | / | ||||
| Cream time (s) | 7~9 | Tensile strength (MPa) | ≥ 5.0 | |||
| Rise time (s) | 10~45 | Elongation (%) | ≥ 450 | |||
| Tack-free time (s) | 50~55 | Tear strength (kN/m) | ≥28.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.4~0.45 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~5 | Folding resistance test (cycles) | 50000 cycles without cracks | |||
| (min) | 23°C, bending 90° | |||||
| ● Optimal dissolving conditions: HT-8211 at 50-60℃ for 10±2 hours; F-2530 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-8255/F-2618 |
| 1. Characteristics: medium-high hardness, good moldability. | ||||||
| 2. Application: Tires, etc. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-8255 | Liquid or wax-like | 1700±400 | 1.02~1.10 | 18 | 6 months | A/B=25/28(Barrel) |
| F-2618 | Liquid or wax-like | 200±50 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-8255 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 250g | 20g | 1200~1500 | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test Item (6mm thick sample) | Reference physical property values | |||
| Reference ratio (weight ratio) | 100/125~127 | Sole molding density | 0.5-0.6 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (°C) | A: 38-42 | Hardness | JISA | 75-85 | ||
| B: 38-42 | ASKER-C | / | ||||
| Cream time (s) | 7~9 | Tensile strength (MPa) | ≥ 4.5 | |||
| Rise time (s) | 10~45 | Elongation (%) | ≥ 400 | |||
| Tack-free time (s) | 50~55 | Tear strength (kN/m) | ≥25.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.4~0.45 | |||
| (℃) | (g/cm³) | |||||
| Demolding time | 3~5 | Folding resistance test (cycles) | 50000 cycles without cracks | |||
| (min) | 23°C, bending 90° | |||||
| ● Optimal dissolving conditions: HT-8255 at 50-60℃ for 10±2 hours; F-2618 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| Resin For Shoe Pad |
| HT-3500/F-2711 |
| 1. Characteristics: low density, low hardness, low temperature resistance, hydrolysis resistance. | ||||||
| 2. Application: Polyether insoles. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-3500 | Liquid or wax-like | 500±200 | 1.00~1.02 | 16 | 6 months | A/B=45/16(Barrel) |
| F-2711 | Liquid or wax-like | 200±100 | 1.12~1.14 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-3500 | SM-2 | Water | Hardener | ||
| Ratio | 16Kg | 450g | 150~170g | |||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/38-42 | Sole molding density | 0.28-0.32 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 35-37 | Hardness | JISA | / | ||
| B: 35-40 | ASKER-C | 22-27 | ||||
| Cream time (s) | 8~12 | Tensile strength (MPa) | ＞0.5 | |||
| Rise time (s) | 13~35 | Elongation (%) | ＞200 | |||
| Tack-free time (s) | 75~80 | |||||
| Metal mold temperature | 45~55 | Free rise density | 0.1~0.11 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 4~7 | |||||
| (min) | ||||||
| ●Optimal dissolving conditions: HT-35001 at 50-60℃ for 10±2 hours; F-2711 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-3571/F-2750 |
| 1. Characteristics: low density, low hardness, low temperature resistance, hydrolysis resistance. | ||||||
| 2. Application: Polyether insoles. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/50℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-3571 | Liquid or wax-like | 500±200 | 1.00~1.02 | 16 | 6 months | A/B=45/14(Barrel) |
| F-2750 | Liquid or wax-like | 200±100 | 1.12~1.14 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-3571 | SM-2 | Water | Hardener | ||
| Ratio | 16Kg | 350g | 110~130g | |||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/36-40 | Sole molding density | 0.28-0.33 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 35-37 | Hardness | JISA | / | ||
| B: 35-40 | ASKER-C | 25-33 | ||||
| Cream time (s) | 8~12 | Tensile strength (MPa) | ＞0.5 | |||
| Rise time (s) | 13~35 | Elongation (%) | ＞200 | |||
| Tack-free time (s) | 75~80 | |||||
| Metal mold temperature | 45~55 | Free rise density | 0.14~0.17 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 4~7 | |||||
| (min) | ||||||
| ●Optimal dissolving conditions: HT-3571 at 50-60℃ for 10±2 hours; F-2750 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-6512/F-2230 |
| 1. Characteristics: low hardness, low density. | ||||||
| 2. Application: Multi-functional, insoles, etc. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-6512 | Liquid or wax-like | 1800±400 | 1.02~1.10 | 18 | 6 months | A/B=30/23(Barrel) |
| F-2230 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-6512 | SM-2 | Water | Hardener | ||
| Ratio | 18Kg | 300~330g | 100~120g | Add appropriately according to hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/76~80 | Sole molding density | 0.3-0.35 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | |||
| B: 40-45 | ASKER-C | 30-50 | ||||
| Cream time (s) | 5~8 | Tensile strength (MPa) | ≥ 3.0 | |||
| Rise time (s) | 9~22 | Elongation (%) | ≥ 400 | |||
| Tack-free time (s) | 30~36 | Tear strength (kN/m) | ≥ 20.0 | |||
| Metal mold temperature | 50~55 | Free rise density | 0.16~0.20 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 3~5 | Flexing resistance test (times) | 30000 cycles without cracks | |||
| (min) | 23℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-6512 at 50-60℃ for 10±2 hours; F-2230 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| Ordinary Polyether Resin |
| HT-3256/F-2730 |
| 1. Characteristics: good elasticity, good anti-slip, medium-high density, low temperature resistance, hydrolysis resistance. | ||||||
| 2. Application: Men's and women's leather shoes, casual shoes. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/50℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-3256 | Liquid or wax-like | 500±200 | 1.00~1.12 | 16 | 6 months | A/B=41/18(Barrel) |
| F-2730 | Liquid or wax-like | 200±100 | 1.12~1.14 | 19 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-3256 | SM-2 | Water | Hardener | ||
| Ratio | 16Kg | 350g | 40~45g | |||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/50-53 | Sole molding density | 0.65-0.8 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 35-37 | Hardness | JISA | 45-50 | ||
| B: 35-40 | ASKER-C | 55-65 | ||||
| Cream time (s) | 8~12 | Tensile strength (MPa) | ＞2.5 | |||
| Rise time (s) | 13~35 | Elongation (%) | ＞300 | |||
| Metal mold temperature | 40~50 | Free rise density | 0.4~0.45 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 7~10 | Tear strength (kN/m) | ＞10 | |||
| (min) | ||||||
| ●Optimal dissolving conditions: HT-3256 at 50-60℃ for 10±2 hours; F-2730 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-3260/F-2750 |
| 1. Characteristics: polyether type, medium-high hardness, low temperature resistance, hydrolysis resistance, excellent anti-slip property. | ||||||
| 2. Application: Production of men's and women's leather shoes and casual shoes. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/40℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-3260 | Liquid or wax-like | 600±200 | 1.02~1.10 | 16 | 6 months | A/B=33/23(Barrel) |
| F-2750 | Liquid or wax-like | 400±200 | 1.18~1.20 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-3260 | SM-2、SM-332 | Water | Hardener | ||
| Ratio | 16Kg | 200~220g 70-90 g | 95-105g | Add appropriately according to hardness | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/88~92 | Sole molding density | 0.55-0.65 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 40-45 | Hardness | JISA | 70-75 | ||
| B: 40-42 | ASKER-C | / | ||||
| Cream time (s) | 5~8 | Tensile strength (MPa) | ≥ 3 | |||
| Rise time (s) | 9~38 | Elongation (%) | ≥ 300 | |||
| Tack-free time (s) | 52~55 | Tear strength (kN/m) | ≥ 20 | |||
| Metal mold temperature | 40~55 | Free rise density | 0.3~0.35 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 4~5 | Flexing resistance test (times) | More than 50000 cycles | |||
| (min) | 23℃, bend 90° | |||||
| ● Optimal dissolving conditions: HT-3260 at 50-60℃ for 10±2 hours; F-2750 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| HT-3268/F-2750 |
| 1. Characteristics: medium-high hardness, medium-high density, low temperature resistance, hydrolysis resistance. | ||||||
| 2. Application: Men's and women's leather shoes, casual shoes, low-load solid tires. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/50℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-3268 | Liquid or wax-like | 500±200 | 1.00~1.12 | 16 | 6 months | A/B=28/26(Barrel) |
| F-2750 | Liquid or wax-like | 200±100 | 1.12~1.14 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-3268 | SM-2 | Water | Hardener | ||
| Ratio | 16Kg | 350g | 80~100g | Add according to needs | ||
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/80-84 | Sole molding density | 0.48-0.55 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 35-37 | Hardness | JISA | 50-54 | ||
| B: 35-40 | ASKER-C | |||||
| Cream time (s) | 7~8 | Tensile strength (MPa) | ＞3.7 | |||
| Rise time (s) | 9~28 | Elongation (%) | ＞340 | |||
| Tack-free time (s) | 30~33 | DIN abrasion (mm3) | 150 | |||
| Metal mold temperature | 45~55 | Free rise density | 0.3~0.25 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 4~7 | Flexing resistance test (times) | 50,000 cycles without cracks | |||
| (min) | 25℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-3268 at 50-60℃ for 10±2 hours; F-2750 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
| Resin For Rain Boots |
| HT-3308/F-2737 |
| 1. Characteristics: medium-low hardness, medium-high density, low temperature resistance, hydrolysis resistance. | ||||||
| 2. Application: Rain boots, casual shoes, low-load solid tires. | ||||||
| 3. Properties of PU matrix | ||||||
| Product name | Appearance | Viscosity | Density | Packaging | Shelf life | Reference shipping ratio: |
| (Pa·s/50℃) | (g/cm³/40℃) | (kg/Barrel) | ||||
| HT-3308 | Liquid or wax-like | 500±200 | 1.00~1.12 | 16 | 6 months | A/B=36/18(Barrel) |
| F-2737 | Liquid or wax-like | 200±100 | 1.12~1.14 | 20 | 3 months | |
| 4. Catalyst and additives: | ||||||
| Category | HT-3308 | SM-2 | SM-6 | Water | Hardener | |
| Ratio | 16Kg | 240g | 80g | 30-50g | 0-300g, it can also be adjusted as needed | |
| Note: The addition of additives is adjusted accordingly for different regions, environments, and production conditions | ||||||
| 5. Molding conditions and physical property value: | ||||||
| Reactivity | Technical parameters | Test item (6mm thick sample) | Reference physical property value | |||
| Reference ratio (weight ratio) | 100/52-57 | Sole molding density | 0.65-0.7 | |||
| (HT+SM)/F | (g/cm³) | |||||
| Operating temperature (℃) | A: 35-37 | Hardness | JISA | 35-42 | ||
| B: 35-40 | ASKER-C | |||||
| Cream time (s) | 12~14 | Tensile strength (MPa) | ＞3..0 | |||
| Rise time (s) | 15~35 | Elongation (%) | ＞300 | |||
| Tack-free time (s) | 75~80 | DIN abrasion (mm3) | 141 | |||
| Metal mold temperature | 45~55 | Free rise density | 0.34~0.36 | |||
| (℃) | (g/cm³) | |||||
| Demoulding time | 4~7 | Flexing resistance test (times) | 50,000 cycles without cracks | |||
| (min) | -30℃, bend 90° | |||||
| ●Optimal dissolving conditions: HT-3308 at 50-60℃ for 10±2 hours; F-2737 at 50-70℃ for 20±4 hours. | ||||||
| ●The mixing ratio is based on the optimal ratio value; this value will vary depending on the type and amount of added pigment and additives. | ||||||
| ●Free foam density will vary according to the season (humidity, temperature), with an approximate variation of around 0.02 based on room temperature (winter, summer). | ||||||
| ●If the density of the cast finished product is relatively low, the mold temperature should be increased to facilitate casting; demolding time will be prolonged as the thickness of the molded product increases. | ||||||
| ●The above data is for reference only; specific data are subject to actual operation. For other physical property requirements, please contact our technical staff. | ||||||
Quick Navigation- Product Center
- Water-based Resins
- Water-based Resins for Leather
- Resins for Leather
- Resins for Shoes
- Polyester Polyols
- Thermoplastic Polyurethane Elastomer (TPU)
- Reactive Polyurethane Hot Melt Adhesive (PUR)
- Solvent-free Polyurethane Lamination Adhesive
- Subsidiaries
- Zhejiang Huada
- Daocheng Chemical
- Jiangsu Huada
- Huada Chemical (Yantai)
- Huada Chemical (Anhui)
- Shandong Huada Chemical New Material
-
Scan and follow the mobile website
Online customer service
Product Center
Contact us
Return to the top